High Tensile PC Wire and Strand

GENERAL

High Tensile Prestressed PC Steel Wire for Concrete Reinforcement is supplied following the standard of ASTM, BS, DIN or per customers’s options. The tensile strength ranges from 1470Mpa-1860Mpa.
According to the tensile strength, pc wire can be classified as: 1470MPa, 1570MPa, 1670MPa, 1770MPa and 1860MPa.
Uses:
Cold drawn steel wire for prestressed concrete strand: Used in prestressed concrete structure reinforced, such as large-span bridges on railway and highway, overhead crane beam, rock-soil anchoring project, multi-storey industrial buildings, stadiums, coal mines and etc.
PC wire, galvanized, ASTM A416-10, 270k, low relaxation, is used for bridge suspension wire and stay-cable applications.
PE coated / covered steel strand: Suitable for large-span and large bays cast-in-place concrete floor, large load of precast beams and other special structure.
Wire Strand Diameter: 4.00mm-12.00mm.

SPECIFIC PRODUCTS

Single PC Wire

High tension single wire for prestressed concrete reinforcement, galvanised 4.8mm (1770Mpa)

High Tensile Strength Seven Wire Steel Strands

Our supply of high tensile strength seven wire steel strands used for pre-stressing of concrete poles for use in electricity distribution as per IS 6006-1983.
Supply through trading comany in Dubai, U.A.E.
Description
Strand shall be made from cold-drawn non-alloy steel (high carbon content) wires. The Seven-wire strand consists of a group of single wires arranged in stranded formation.
Geometrical Properties
The seven-wire strand shall have the following geometrical properties:
Type of meterial: Seven-wire steel strand
Nominal diamater of strand: 7.9 mm (7/2.6 mm)
Tolerance on the nominal diamater of strand: +0.4 mm
Nominal cross-sectional area of strand: 37.4mm2
Mechanical Properties
Nominal mass of strand: 294 g/m
Minimum Breaking Load: 64.50 kN
0.2% proof load: 54.70 kN
Long-term behaviour
Maximum relaxation after 1000h of operation at initial load equivalent to 60%, 70% and 80%
of breaking load shall be as per IS 6006-1983 (Amendment January 1988)
Technological properties
The finished materials shall be free from defects, which may have occurred at any stage of manufacture, to a dergee that would impair the performance as a per-stressing tendon.
Rusted steels, apart form those with a thin film of rust, shall not be supplied.
The normal production length may contain welds made in individual wires before drawing, but shall not contain any welds made during or after wire drawing. Not more than one weld shall be permitted in any 50m of strand. The strand-forming operations and the stress-relieving treatment shall ensure that the wires do not unravel when the strand is cut.

7mm diameter P.C Wire - HT Stranded Wire
We supply Turkey contractor for electromechanical projects and the civil contractors in Africa 7mm diameter P.C Wire, as following specification.

1860 MPa 7mm diameter High Tensile Steel  P.C Wire, for Cement Plant in Tanzania, Africa.
Technical Specification of 7mm diameter High Tensile Steel Wire with Spiral Ribs ( Standard JIS G 3536 )
Nominal Diameter : 7 mm diameter 
Theoretical Weight: 302 gm/m 
Sectional Area : 38.48 mm2 
Diameter Tolerance :± 0.05
Mechanical Properties 
0.2% Proof Load ( min: ): 50.995 KN 
Breaking Load ( min: ): 58.35 KN 
Elongation ( min: ) : 4.5 %
Relaxation value ( max: ) : 3.00 %

PC Steel Wire of 7mm & 5mm OD, Tensile Strength: 1670MPA
Details:

Tensile: 1670MPA
Relaxation: low relaxation
Supply to India

5mm (1770Mpa) and 7mm (1670Mpa) PC Wire for CIF Port Klang.

4mm, 4.8mm, 5mm, 6mm, 7mm PC wire Supply to Malaysia

12.70MM LRPC Strand
Specification : As per ASTM A-416, Grade : 270
Tensile Strength : 1860Mpa (Min.)
Relaxation: Low relaxation
Coil Weight : 2500-3000Kgs/Coil