The term "washing" can be defined as &#;removing a substance by or as by the action of water&#;. In a mineral processing sense, washing commonly refers to the removal of loosely attached particles &#; often fine clays &#; from the surface of more competent ore.
In this definition, washing is distinct from classification, which would be a subsequent processing step that separates the different sized fractions.
Despite increasing concerns about the value and availability of water, ore washing remains a common and cost-effective means of beneficiation, as water usage is enhanced by the greater use of water recovery.
Advantages of scrubbing ore can include the reduction of gangue to process further, improved product quality and higher throughput of downstream equipment.
Although generally thought of as removing waste material, in highly weathered deposits, the inverse may apply and the valuable mineral be contained in the fines. Examples occur in alumina, nickel laterites, uranium and occasionally gold.
The over-riding principle in ore washing is to provide sufficient energy and time to detach the fine clays but not enough to cause comminution of the intrinsic particles to smaller components.
Care also needs to be exercised to provide appropriate energy and flow to maintain the fine particles in suspension and not allow them to agglomerate and grow as clay balls. Thus, defining a suitable ore washing process should consider the following:
Sizing ore washing equipment is largely empirically based on scale-up of laboratory or pilot tests, and subsequently benchmarked off operating installations.
The high degree of variability in clay mineralogy leads to a preference to do site-specific testing. Standards such as ASTM D-17, ASTM D-17 and ASTM D-03 exist to help define the plasticity and/or the dispersive characteristic of clay materials and aggregate durability, but to date, a measurable correlation between these and energy input has not been published.
Test work is commonly carried out in either commercial testing laboratories or by vendors. McLanahan Corporation has facilities in Australia (New South Wales) and United States (Pennsylvania) for in-house materials testing.
Equipment used for testing can vary from scaled-down vendor equipment, adapted commercially available substitutes, equipment designed for alternative testing to purpose-built pilot plants capable of taking full-size range.
A major limitation with all but purpose-built pilot plants is the ability to process a representative sample size range, particularly for those duties with a feed size of up to 10" (250mm).
Most small-scale test work is done on a batch basis. This can create some interpretation issues. It is generally acknowledged the batch testing provides an indication of the required solids residence time; however, most equipment is operated in a continuous mode.
Subject to the geometry and flow patterns within the equipment, the fluid phase will traverse at a different rate. As such, residence time distributions of both the liquid and solid phases must be accounted for.
Common design specifications refer only to an average residence time, hence evaluation of the equipment used for testing is critical for establishing design parameters.
Discrete Element Model (DEM) using computer simulation has been successfully used to approximate both residence time and power draw on a comparative scale when calibrated against known installation.
Once energy requirement, particle size, residence time and throughput are established, the following matrix can provide a guideline for equipment selection.
Attrition Cells are high-energy devices used to liberate tough-plastic deleterious material and remove it from competent material. They are also proven to liberate clays, reducing product turbidity, and to break apart loosely conglomerated clusters.
These machines are primarily comprised of a tank (cell) in which a vertical shaft drives a set of two to three diametrically opposed mixer blades. The cell itself can be round, square, hexagonal or octagonal, but all are generally baffled to an extent to minimize swirling. The configuration of the blades can be simple axial turbine or propeller in design.
As the blades rotate, material is forced against itself to cause particle-on-particle collisions, thus abrading the surfaces and liberating the coating material.
Because of the intense mixing action, the particle residence time distribution in any one cell can be quite broad, with some particles leaving the cell quickly (bypass) and others remaining for longer durations.
To help improve the bypass, Attrition Cells are commonly supplied as multiple cells, with two to four cells per machine being most common. Often, alternating cells in series like this will have reversed the pitch of the impeller blades to aid direction of the flow toward the outlet at either the top or bottom of the tank.
Weirs at the final discharge lip allow the operator to adjust the height of the slurry within the tank and hence increase or decrease residence time.
Attrition Cells are typically fed at high solids (60-80% solids by mass). As such, upstream unit operations will commonly consist of dewatering cyclones or even dewatering screens. These present the material at a high density to achieve maximum particle-on-particle scrubbing action.
The feed size is limited to around 1/4" (6mm) for materials in the range of 2.7 specific gravity. Because the attritioning efficiency is greater at higher solids concentrations, one must be careful not to run the machine into an operating environment that causes plugging. Monitoring of the power input can assist in operating in a more desirable region with simple water addition on demand.
It is also important to understand any changes in the state of the slurry as the attritioning process takes effect. In instances where there is a presence of high clays, or clays that only become broken down and suspended after high shear, the slurry itself may take on an oatmeal-like consistency. The resulting effect is that the competent particles are well lubricated in the mass and further attritioning is impeded.
The solution to this is to use an inter-stage wash operation between sets of attrition cell units. These wash circuits remove the liberated clays and return the remaining competent particles to downstream attritioning. To help reduce water consumption by the wash stages, a counter-current approach is often recommended, with the dirtiest discharges being washed with the dirtiest water.
Due to the high shear environment, it is important to have suitable wear protection (rubber-lining and/or hardened steels) to maximize life and minimize time and costs of replacement parts.
Attrition cells are used in glass, heavy mineral and frac sand industries to provide intensive scrubbing (Preston & Tatarzyn ), with an energy input of 5-10 kWh/t. To accommodate the high energy, these are small units of 1-10 m3 commonly fitted with a direct drive motor. Residence times may range from 0.5 - 5 minutes.
Coarse Material Screw Washers are built primarily to wash crushed stone, gravel and other hard ore minerals, generally ranging from 3/8" (10mm) to 4"(100mm). They effectively remove light loamy-type clays, dirt, crusher dust and coatings that cannot be removed by wet screening alone.
They also can be used to take out floating vegetation and soft aggregate, although all vegetation and water-logged sticks may not be removed completely. Coarse Material Screw Washers are not intended to remove the tough plastic clay that normally requires a more energy intensive machine.
On Coarse Material Screw Washers, paddles are used in conjunction with screw flights to provide scrubbing, scouring and agitation. The turbulent washing action combined with rising current water introduced at the bottom of the box at the feed end results in separation of the lighter fraction from the sound aggregate.
The lighter fraction (i.e. clay and floating vegetation) rises to the surface due to the water rising in the box and then overflows the weir located in the back of the box. The desired clean product is then scrubbed and conveyed by the paddles and flights to the discharge end of the box.
A rinsing screen is recommended for use after the Coarse Material Screw Washer to provide the material classification.
The sizing and selection of a Coarse Material Screw Washer is based on the type of material, desired capacity and maximum feed size. The more paddles that are used, the lower the capacity; however, the washing action is increased due to the fact that paddles do not convey material up the washer box as fast as spiral flights.
A Coarse Material Screw Washer can be furnished with up to 40 paddles per shaft. When using additional paddles, it is also necessary to lower the slope of the box and increase motor horsepower. This will help convey material to the discharge end.
Subject to the duty, either volumetric and solids capacity limitations may see twin screw units employed. The larger pool area on the twin screw unit will lower the rise rate, resulting in a finer classification, and the double screw will permit a higher solids loading.
The screw shaft is composed of an extra-heavy steel pipe shaft with inner and outer renewable and reversible abrasion-resistant hard iron paddles bolted to the shaft in the feed area. These paddles are preceded and followed by heavy steel flights equipped with bolt-on abrasion resistant liners. The screw shaft is flanged at both ends and bolted to stub shafts to facilitate normal maintenance.
Log Washers are used in a variety of material processing applications and are best known for their ability to remove tough, plastic clays from natural and crushed gravel, crushed stone, and ore feeds.
One limitation of Log Washers is that they must have a controlled top size. In general, most units can accept feed material up to 4&#; (100mm) cubed, though some larger diameter units can accept a feed material up to 6&#; (150mm) cubed.
When processing fines, it may be necessary to capture the overflow of the unit to save this fraction for further processing or close off the overflow opening so that material is carried the full length of the box for scouring of the fines.
When selecting a Log Washer for an application, the amount, type and percentage of deleterious material (i.e. clay) to be removed should be considered. As the percentage of deleterious material to be removed increases, options exist to:
Most Log Washers come standard with adjustable weirs at the overflow openings that permit the change in water depth, which, in turn, can affect the quality of the washed product. They are often equipped with a spray bar for rinsing the material prior to discharge.
Critical to the reliability of a Log Washer is the need for a robust design of the washer box, log shafts, gear box/drive train and the submerged rear bearings.
Maintenance is required on the submerged bearing and wearing surfaces for the paddles. The paddles are often provided with replaceable wear shoes.
Blade Mills, also known as Conditioners, are designed to help producers begin liberating light, loamy clay or dirt from either coarse rock and/or sand before further processing.
There are many applications where a Blade Mill can be used. As an example, when washing coarse rock, the Blade Mill could be placed ahead of a wash screen resulting in cleaner rock or ore. When washing finer materials such as sand, the unit could be placed ahead of a screen, Sand Classifying Tank or Fine Material Screw Washer.
Blade Mills are able to accept either coarse or fine feed material.
Keep in mind that Blade Mills are designed to condition. They are not designed to remove tough, plastic clay or high percentages of clay. Blade Mills usually are selected for use with other processing equipment to improve the downstream washing and separation of material.
Due to all the material and water exiting the unit, the discharge material cannot be fed onto a conveyor belt. Generally, the amount of water needed for a Blade Mill is an additional third of the weight of material being processed.
Blade Mills are very similar in appearance to Coarse Material Screw Washers but function much differently. The major difference is that any material and water that enters the Blade Mill must exit through the discharge opening located at the bottom of the box opposite the feed end. There is no overflow in this type of unit.
Using a combination of paddles and flights arranged in alternating format the entire length of the shaft, they begin to scour, abrade and break down deleterious material. The shafts can have different configurations but mainly the idea is to have alternating flights and paddles.
Blade Mills sit on a slope of 0° to 5° and have higher capacities as compared to the same size Coarse Material Screw Washers. This is due to the lower machine operating slope.
Again, a Blade Mill is used where the material needs to be worked or wetted before it enters a vibrating screen, Fine Material Screw Washer or other wet processing equipment.
Rotary Scrubbers are designed primarily for the removal of loam and light clays and soft, soluble waste materials from aggregates, stone and ore.
Scrubbers are not intended to replace Log Washers in applications where tough plastic clays are contaminating the material to be cleaned. When these tough clays are fed to a Scrubber, the clay particles may have a tendency to pelletize through the tumbling action of the material.
For example, golf ball size pieces of plastic clay may not break down and have been known increase to the size of a tennis ball.
Scrubbers and Coarse Material Screw Washers are often selected to wash out similar contaminants from aggregate and various ores. The major difference is that Scrubbers can accept larger feed sizes, whereas Coarse Material Screw Washers must have a controlled top size.
Additionally, Scrubbers have much higher throughput capacity. Since large diameter Scrubbers can handle feeds up to 10-12&#; (250-300mm), they are sometimes used as a primary washer before any crushing or screening is accomplished.
For long residence times and low energies, a smaller diameter, longer machine is most effective. For short residence times and high input energies, larger diameter, shorter machines are more effective.
Capacities are normally determined by analyzing the type of feed material, percent and type of waste material to be removed, a screen analysis of the feed, and available water. The required retention time will vary in a Scrubber for each application due to different types and varying amounts of wastes to be removed. Testing will help establish guidelines required.
Rotary Scrubbers may range in diameter from 8' (2.5m) to 18' (5.0m) and lengths from 8' (2.5m) to 60' (18m) with aspect ratios (L/D) ranging from 1.8 to 3.0. Scrubbers can be sized to process up to 5,000 tph of ore.
Improved washing can be accomplished by
The selection of an appropriate drive mechanism depends on the power and variability required. Small units may use a friction, chain or rubber tire drive system. These styles are limited in power to 300-500 kW and approximately 10' (3m) diameter.
Larger units may use an end drive stub-mounted hydraulic motor or girth gear with pinion. Power intensity required in most scrubbing duties ranges from 0.2 &#; 1.0 kWh/t.
Support systems offered include trunnion rollers with steel, rubber or polyurethane tires or hydrostatic bearing pads similar to ball mills.
Rotary Scrubbers work by having process water and solids introduced through the feed chute. As the cylinder rotates, the solid feed fraction is carried up the side of the drum by centrifugal force until its surface reaches the dynamic angle of repose &#; typically in the range of 35° to 45°.
The surface material then cascades and tumbles to the bottom of the solids pile before being carried back under the pile by the rotating drum.
Lifter bars on the drum shell ensure that the solids pile cascades and tumbles rather than sliding down the wall. This action helps to break down the softer materials and liberates clays, dirt, loam and other foreign materials into solution.
For special washing and screening applications, a combination Scrubber-Screen may be used. These units combine the scrubbing characteristics of a Rotary Scrubber with the screening portion of Rotary Trommel Screens &#; all in one unit. The screen portion can be supplied either with a single or double shell design.
Scrubber-Screens can be effective when handling hard-to-wash-and-screen materials, such as oyster shells and phosphate matrix, and offer some benefits in plant layout options.
The maintenance required on Rotary Drum Scrubbers will vary according to the size, hardness, throughput and abrasiveness of the material being processed. Replaceable liners on the feed chute shell and end wall can be changed at intervals of 12-36 months.
Want more information on Mineral Separation Equipment? Feel free to contact us.